12 mm recycled HDPE Tank Covers Vacuum Forming for Beauty And Spa Equipment

Vacuum formed tank covers are used across beauty and spa equipment because they can be produced without the tooling spend of injection moulding and without the weight of sheet metal. This page covers how 12 mm recycled HDPE sheet is formed for beauty and spa equipment, what tolerances are realistic, and what has to be on the drawing before tooling starts.

The route below is the one used for most of the tank covers shipped from this plant: sheet is heated on the forming machine, drawn over an aluminium or composite mould, cooled on a jig, then trimmed on a 5-axis router. For tank covers the sheet gauge is selected from the load case rather than from habit, and recycled HDPE is the material most often specified for this combination.

Typical specification

Where these parts are used

• lamp covers for beauty and spa equipment
• trolley trays for beauty and spa equipment
• treatment bed shells for beauty and spa equipment
• device housings for beauty and spa equipment
• tank covers in general beauty and spa equipment builds

How the part is made

1. Drawings are reviewed and a manufacturability report is issued with wall thickness, draft and radii marked up.
2. Tooling is cut: aluminium for production volumes, composite or printed moulds for samples and first articles.
3. Sheet is dried when the material needs it, then heated to forming temperature on the machine.
4. The sheet is formed over the mould with vacuum and, where the draw is deep, with plug assist.
5. The part cools on a jig so the shape is held while the material stabilises.
6. Trimming is done on 5-axis routers or with a dedicated trim fixture to meet the drawing.
7. Parts are inspected, fitted with inserts or hardware if required, packed and shipped.

Material notes: recycled HDPE

Recycled HDPE sheet lowers material cost and supports sustainability targets, with mechanical properties close to virgin sheet for non critical parts.

Design tips for this part

• keep a draft angle of at least 3 degrees on vertical walls so the part releases cleanly
• hold the draw ratio near 1:1 for deep parts, or specify plug assist
• avoid sharp steps in the mould, which show as chill marks on the finished surface
• plan the trim line on a flat face so the router can hold tolerance
• use corner radii of at least three times the sheet thickness to avoid thinning

Quality and inspection

Batch releases carry a dimensional report, material certificate and, where agreed, PPAP or ISIR documentation. First article inspection covers critical dimensions, wall thickness, colour and texture against the approved sample.

Cost and lead time

Tooling is the main cost driver at low volume, so a 12 mm tank covers for beauty and spa equipment is usually quoted with a composite or printed mould first and the aluminium tool cut once the design is frozen. That keeps the first article cost low and gives a real part to test before the production tool exists. The result is corrosion resistance compared with the alternatives, and a piece price that stays stable across repeat releases.

• Sample tooling: 7–15 working days
• Production tooling: 3–4 weeks
• Repeat orders run on stored tooling with no new proving run

Frequently asked questions

What do you need to quote?

A 3D file or drawing, the material if it is fixed, the annual quantity and the finish. Photos of the current part are enough for a first estimate.

Can you match an existing part?

Yes. Send a sample or scan and the part can be reverse engineered, with the wall thickness and material measured from the sample.

What quantities make sense?

Vacuum forming pays off from roughly 25 pieces up to several thousand a year. Below that, printed or composite tooling keeps the setup cost low.

Getting started

Send the drawing or a photo of the current tank covers with the quantity and the finish. The first reply is a manufacturability review with the wall thickness, material and a quotation, so the decision is made on facts rather than on a price alone.