polycarbonate Equipment Covers Vacuum Formed in 5 mm for Catering And Kitchen Equipment

These polycarbonate equipment covers are thick gauge vacuum formed parts supplied to drawing for catering and kitchen equipment. They are formed from polycarbonate sheet at 5 mm, trimmed on 5-axis routers and inspected against the drawing before packing. Buyers choose this route where a metal fabrication is too heavy, or where injection moulding tooling cannot be justified for the volume.

Product specification

Key features

• One piece shell replaces a fabrication, so assembly hours drop
• polycarbonate keeps the weight down while stiffness is held through the formed shape
• As formed gloss finish as standard, further finishes on request
• Trimmed on 5-axis routers, so mounting holes and cut outs match the drawing
• Tooling stored against the part number for repeat and spare orders
• RoHS compliant grades available

Typical applications

• bain marie liners
• hood panels
• service trolley trays
• refrigerated well covers
• equipment covers used across general catering and kitchen equipment builds

How it is made

1. The part cools on a jig so the shape is held while the material stabilises.
2. Drawings are reviewed and a manufacturability report is issued with wall thickness, draft and radii marked up.
3. Trimming is done on 5-axis routers or with a dedicated trim fixture to meet the drawing.
4. Parts are inspected, fitted with inserts or hardware if required, packed and shipped.
5. Sheet is dried when the material needs it, then heated to forming temperature on the machine.

Material: polycarbonate

Polycarbonate is used when the housing must survive impact or carry a glazing function. It must be dried before forming or the sheet will bubble.

Design notes

• call out the finish on the drawing: mould texture, paint, or as-formed gloss
• hold the draw ratio near 1:1 for deep parts, or specify plug assist
• keep a draft angle of at least 3 degrees on vertical walls so the part releases cleanly
• add ribs or returns instead of increasing sheet thickness to save weight and cycle time

Finishing and assembly options

• as formed gloss
• UV stabilised as formed
• powder coat finish
• Threaded inserts, PEM fasteners and brackets fitted before dispatch
• Mating parts can be trial assembled before the first article ships

Quality

First article inspection covers critical dimensions, wall thickness, colour and texture against the approved sample. Sheet thickness is checked on the formed part at the points shown on the drawing, and the readings go into the report.

• RoHS compliant grades available
• UL94 V-0 grades available
• material certificates with every batch

Packing and delivery

Parts are nested to save freight, with returnable dunnage available on repeat routes. Standard lead time to first article is 2–3 weeks, and repeat releases ship against stored tooling without a new proving run.

Frequently asked questions

How fast is the first article?

Seven to fifteen working days from drawing release for sample tooling, with production tooling in three to four weeks.

Are spare parts available later?

Tooling is stored against the part number for the life of the programme, so replacements or spare panels can be released at any time.

What quantity can I order?

Sample quantities start at one piece off printed tooling. The process pays back from about 25 pieces a year and runs well into several thousand.

Request a quotation

Send the drawing or a photo of the current equipment covers with the quantity and the finish required. The reply covers material choice, wall thickness, tooling route and price, so the decision is made on a complete picture.