Skid Plates HDPE in 8 mm for Fitness Equipment – Formed to Drawing

These HDPE skid plates are thick gauge vacuum formed parts supplied to drawing for fitness equipment. They are formed from HDPE sheet at 8 mm, trimmed on 5-axis routers and inspected against the drawing before packing. Buyers choose this route where a metal fabrication is too heavy, or where injection moulding tooling cannot be justified for the volume.

Product specification

Key features

• One piece shell replaces a fabrication, so assembly hours drop
• HDPE keeps the weight down while stiffness is held through the formed shape
• Emi shielding coating finish as standard, further finishes on request
• Trimmed on 5-axis routers, so mounting holes and cut outs match the drawing
• Tooling stored against the part number for repeat and spare orders
• UL94 V-0 grades available

Typical applications

• seat shells
• weight stack shrouds
• treadmill motor covers
• console housings
• skid plates used across general fitness equipment builds

How it is made

1. The sheet is formed over the mould with vacuum and, where the draw is deep, with plug assist.
2. Drawings are reviewed and a manufacturability report is issued with wall thickness, draft and radii marked up.
3. Sheet is dried when the material needs it, then heated to forming temperature on the machine.
4. Trimming is done on 5-axis routers or with a dedicated trim fixture to meet the drawing.
5. Parts are inspected, fitted with inserts or hardware if required, packed and shipped.

Material: HDPE

HDPE is chosen for chemical resistance and impact strength at low temperature. It needs more heat and a longer cooling cycle than ABS, and it is painted only after flame or plasma treatment.

Design notes

• keep a draft angle of at least 3 degrees on vertical walls so the part releases cleanly
• plan the trim line on a flat face so the router can hold tolerance
• use corner radii of at least three times the sheet thickness to avoid thinning
• add ribs or returns instead of increasing sheet thickness to save weight and cycle time

Finishing and assembly options

• EMI shielding coating
• UV stabilised as formed
• powder coat finish
• Threaded inserts, PEM fasteners and brackets fitted before dispatch
• Mating parts can be trial assembled before the first article ships

Quality

First article inspection covers critical dimensions, wall thickness, colour and texture against the approved sample. Sheet thickness is checked on the formed part at the points shown on the drawing, and the readings go into the report.

• food contact declarations available
• RoHS compliant grades available
• dimension reports with every release

Packing and delivery

Parts are stacked with interleaved film and packed in export cartons on pallets. Standard lead time to first article is 3–4 weeks, and repeat releases ship against stored tooling without a new proving run.

Frequently asked questions

Are spare parts available later?

Tooling is stored against the part number for the life of the programme, so replacements or spare panels can be released at any time.

What quantity can I order?

Sample quantities start at one piece off printed tooling. The process pays back from about 25 pieces a year and runs well into several thousand.

Can you make it in another material?

Any grade in this family can be swapped in. Send the requirement and the material will be quoted with the price difference shown.

Request a quotation

Send the drawing or a photo of the current skid plates with the quantity and the finish required. The reply covers material choice, wall thickness, tooling route and price, so the decision is made on a complete picture.